PROPERTIES OF UNCURED MATERIAL 固化前材料性能
|
Property
性能
|
Test Method
測試方法
|
|
|
|
Color/appearance
顏色/外觀
|
Visual
|
Yellow,
黃色
|
Blue,
藍色
|
|
Specific gravity
密度, g/cc
|
ASTM D-792
|
1.23
|
1.1
|
|
Viscosity
粘度 (cP), 25ºC
|
ASTM D-2393
|
Soft thixotropy
柔性觸變膏體
|
Soft thixotropy
柔性觸變膏體
|
TYPICAL PROPERTIES OF CURED MATERIAL 固化后材料典型物理性能
|
Property
性能
|
Test Method
測試方法
|
Typical Value
典型值
|
|
Tensile Strength
抗拉強度, N/mm2
|
ASTM D-638
|
71( 23°C)
24 ( 60°C)
|
|
Elongation 延長率 (%)
|
ASTM D-638
|
3
|
|
Modulus
模量 N/mm2
|
|
4050 ( 23°C) 2400 (60°C)
|
|
Impact Strength 沖擊強度, J/m2
|
K 1C
|
2
|
|
Glass Transition Temperature
玻璃化轉變溫度, Tg per DSC, °C
|
ASTM D-4065
|
78
|
|
Heat Distortion Temperature
熱變形溫度, °C
|
|
70-75
|
|
Coefficient of Thermal Expansion
熱膨脹系數, (in/in/°C), -50°C to +50°C
|
ASTM E-831
|
58 X 10-6
|
|
Curing Shrinkage收縮率, %
|
|
0.2
|
|
Roller Peel Strength 滾筒剝離強度, N/mm
|
ISO 4578
|
6
|
|
Lap shear strength 層間剪切強度, N/mm2
|
ASTM D-1002
|
|
|
Stainless Steel (grit blasted) 不銹鋼（磨砂處理）
|
|
25
|
|
FRP Prepreg FRP預浸漬
|
|
11
|
|
Aluminum ( acid etched)鋁（酸腐蝕）
|
30
|
|
|
Aluminum ( Chromate surface treated)
鋁（鉻酸鹽表面處理）
|
Tested at -60 °C
|
20
|
|
Tested at 23 °C
|
25
|
|
|
Tested at 70 °C
|
21
|
|
|
Tested at 80 °C
|
18
|
|
|
Tested at 90 °C
|
11
|
|
|
Tested at 100 °C
|
8
|
|
|
Double lap shear strength, Epoxy Laminate
雙層剪切強度, 環氧層壓板, N/mm2
|
Tested at -20 °C
|
15
|
|
Tested at 23 °C
|
17
|
|
|
Tested at 50 °C
|
17
|
|
|
Environmental Resistance 耐候性
|
Immersion 浸漬
|
Strength 強度
|
|
90 days in lubricate oil 潤滑油中90天
|
|
Slight change
輕微改變
|
|
90 days in fuel 燃油中90天
|
|
No change無變化
|
|
90 days in water at ambient condition 水中90天
|
|
No change無變化
|
|
90 days in tropical humidity 濕熱90天
|
|
Slight change
輕微改變
|
DIRECTIONS FOR USE 使用指南
|
Mix Ratio (by weight) 樹脂與固化劑重量比
|
100R/33H
|
|
Mix Ratio (by volume) 樹脂與固化劑體積比
|
100R/40H
|
|
Pot Life (100 grams) 保質期（100g）, 25°C
|
4 hours
|
|
5cm radius bead 5cm 半徑的球狀, 25°C
|
2 hours
|
Curing time table 固化進度表：
Curing at 70℃ ×4 hours is recommended. 推薦固化溫度70 ℃下固化4個小時。
|
Curing temperature固化溫度
|
Curing time
固化時間（到1N/mm2）
|
Curing time
固化時間（到10N/mm2）
|
|
23 ℃
|
15 h
|
75 h
|
|
60 ℃
|
1.5 h
|
3 h
|