Used for high-performance ignition temperature curing epoxy adhesive in 1000A/1200B
 
I. Introduction:

1000A/1200B high performance epoxy adhesive is transparent, with toughness, low hardness, heat-curing two component epoxy resin injection, it is with engineering plastics, ceramic substrates with excellent adhesion, is an ideal package material; especially suitable for hot and cold shock of the occasion required. 

I. Features:

a) low viscosity, good casting process;

b) good resistance to thermal shock can reach -55 ℃ ~ +120 ℃ cycle shocks;

c) excellent electrical insulation, mechanical and physical properties.

Second, the conventional performance:

Test Project
 Testing methods or conditions
 1000A
 1200B
 
Appearance
 Head Measurement
 Color and transparent
 Light brown
 
Viscosity
 40 ℃, mpa · s
 800 ~ 1300
 700 ~ 1500
 
Density
 25 ℃, g/cm3
 1.1 ~ 1.2
 1.3 ~ 1.4
 
Use of time
 35 ℃, hrs
 3.5
 
Gel time
 150 ℃, 1g, s
 170 200 
 
Fourth, use:
For high pressure gas ignition, transformers, high-performance electronic components modules and other special packages.

*: Our products 1000A/1200B is a new imported resin, this product is a client specifically for our European and Middle East customer for the gas ignition coil designed for potting resin, silica powder was added for customers to use a low cost of production the product after pressure casting, the products, sub-series circuit design, product pressure and thus reached the 4 to 5 million volts / mm.

Fifth, use of technology:

Test Project
 Testing methods or conditions
 1000A/1200B
 
With more than
 Weight ratio
 100:120
 
Curing conditions
 ℃ / hrs
 100 / 4
 
Recommended curing conditions
 40 ~ 55 degrees / +80 degrees 1 hour defoaming / 4 hour +100 degrees / +120 degrees 2 hours / 3 hours, oven cooling 
 
VI characteristics of atherosclerotic *:

Item
 Units or conditions
 1000A/1200B
 Reference standard (ASTM D)
 
Appearance
 /
 Transparent color
 Visual method
 
Hardness
 Shore-D
 60 ~ 70
 2240
 
Volume resistivity
 25 ℃, Ω · cm
 > 3.2 × 1015
 150
 
Dielectric Strength
 25 ℃, kV / mm
 > 24
 149
 
K
 25 ℃, 1MHZ
 3.7 ± 0.1
 150
 
Dielectric loss tangent
 25 ℃, 1MHZ,%
 <1.2
 257
 
Impact strength
 kJ/m2
 > 34
 780
 
Water absorption
 %
 <0.04
 570
 
Elongation
 %
 > 250
 638
 

    * The above parameters are 1000A/1200B ratio of 100:120, curing time is 100 ℃ / 4hrs later measured.

VII, storage, transportation and precautions:

1. 1000A/1200B should be stored in dry, ventilated room. Open the unused material, the lid should Gaiyan to prevent absorption of moisture deterioration. Six months from the date of manufacture is valid, more than shelf life, regular features to be checked and qualified before being used.

2. Such products as non-dangerous goods, according to general chemical storage and transportation.

3. In use, the operating staff should be protective measures, accidentally touches the skin or eyes face, must be promptly cleaned with a mild soap or a medical practitioner for treatment.

VIII, packaging specifications:

A, B are 20KG metal containers or specified packaging, packaging should be manufacturer, batch number, net weight, quality certification mark.

Ú Note: The above performance data for the product in 70% humidity, temperature 25 ℃, the typical test data for reference purposes only customers, and can not guarantee that a particular environment can be achieved when all the data. Please use customers, subject to the measured data.